| Carbon Content: | High-Carbon |
|---|---|
| Bulk Density: | 1.72gdfs/Cm3 |
| Specific-Resistance: | 9 |
| Compressive-Strength: | 30MPa |
| Flexural-Strength: | 13MPa |
| C.T.E.(Rt-600ºC): | 3.2/ºC |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier
| Grade | MV-13 | |
| Material | Vibration Molded Graphite | |
| Specifications | Unit | Typical Value |
| Bulk Density | g/cm3 | 1.73 |
| Specific Resistance | μΩ.m | 8.5 |
| Compressive Strength | MPa | 35 |
| Flexural Strength | MPa | 15 |
| C.T.E.(RT-600ºC) | 10~6/ºC | 3.3 |
| Thermal Conductivity | W/(m.k) | 130 |
| Ash Content | % | 0.12 |
| Maximum Grain Size | mm | 0.8 |
Size |
510×510×1830mm,550×510×2200mm 650×510×1830mm,650×510×2200mm 650×610×1830mm,650×610×2200mm 710×510×2500mm,760×510×1830mm 820×410×1830mm,820×510×1830mm 810×510×2230mm,950×510×1900mm 1050×450×2100mm,1120×450×2230mm 1300×450×2550mm,φ820×650mm 850×650mm,0920×640mm 01000×590-660mm,φ1120×410mm 01120×590mm,φ1270-×410mm 01270×600mm,1300×600mm 01420×410-590mm,φ1590×590mm 01800×520mm |
|
The casting industry in the machinery industry uses vibration graphite materials as centrifugal casting molds in large quantities for the following reasons:
High thermal conductivity: graphite material has high thermal conductivity, can quickly transfer heat, so that the metal liquid inside the casting mold solidifies quickly, so as to improve the casting's density and mechanical properties.
High heat resistance: graphite material can maintain stable chemical properties at high temperatures, will not react with the metal liquid, and will not be eroded by the metal liquid, to ensure the quality of the castings.
Excellent mechanical properties: graphite material has excellent mechanical properties such as high strength, high hardness, high wear resistance, etc. It can meet the requirements of high strength, high hardness and high wear resistance of centrifugal casting processing.
Easy to process: graphite material is easy to process into various shapes and sizes of molds, which can meet the needs of different castings. In addition, graphite molds have a long service life and can be reused many times after proper maintenance, effectively reducing production costs.
Good lubrication performance: graphite material has good lubrication performance, which can reduce the friction between casting and metal liquid, thus prolonging the service life of the mold.
Environmental protection: graphite material is an environmentally friendly material, which does not produce harmful gases at high temperatures and does not pollute the environment. In addition, the use of graphite molds can reduce metal waste, which is conducive to the sustainable use of resources.
SHJ MV series vibration molded graphite material is pressed by vibration molding process, and the molded graphite has exactly the same performance value in different directions. It has a series of excellent characteristics, which makes it closely associated with today's high technology and defense technology.
Commonly used in the manufacture of single crystal furnace graphite hot field, metal continuous casting graphite crystallizer and EDM graphite electrodes. Our products have stable performance and are sold well at home and abroad, and are loved and supported by our customers.